Huisins New Material Technology Co., Limited,
|
Gold Index: 7063
Metal Surface Steel Spray Paint Water - Resistant Paint Acrylic Polymer Coating
| Place of Origin: | Zhejiang, China (Mainland) |
|
|
| Add to My Favorites | |
| HiSupplier Escrow |
Product Detail
Metal Surface Steel Spray Paint Water - Resistant Paint
Metal Surface Steel Spray Paint Water - Resistant Paint Acrylic Polymer Coating
Industrial enterprises, especial of the petrochemicals are the focus protection from fire and explosion
risks. Most of the recent industry anticorrosion coatings are oil base with solvent evaporation in the
performance procedure then caused to great security trouble. Therefore, the anticorrosion performance
in industrial enterprises is mostly operated at close states which are also affecting the normal production.
According to this situation, SWD Urethane Co., USA actively scientific research, developed water base
metal protective anticorrosion coating. This product has 0 VOC content can be operated in the normal
production state of the industrial enterprises without risks.
Characteristics The coating applies one component environment friendly water base high molecule polymer resin. The
film of coating is dense and tough with stable performances of acid resistance, alkali resistance, salt
resistance, oil resistance, water resistance and chemical media resistance. No crack, no peel off and
no fall down after long term outdoor application the coating can bear alternating impact of hot and cold
and various weather influences in wind, frost , snow, rain, etc.
Feature:
1, Safety and environmental friendly;
2, High solid content and large besmear brushs area;
3, Excellent antirust resistance; Good adhesion;
4, Weather resistance, water resistance and good color retention;
5, Fast dry; Film tough, resistant to impact.
Specifications:
|
Product Name |
Water-based Steel Spray Paint For Anti-rust Protection Grates |
|
Density |
1.20g/cm |
|
Volume solid content |
40%+/- 2% |
|
VOC |
20g/L |
|
Recommended dry film thickness |
45-100um |
|
Theoretical coverage |
0.19kg/sgm (calculated by the above solids percentage and dry film thickness of 100microns) |
|
Viscosity |
30s |
|
Pencil hardness |
H |
|
Salt water resistance |
240Hrs |
|
Practical coverage |
Allow appropriate loss rate |
|
Curing mechanism |
Room Temperature cure |
|
Tack free time |
1-3Hrs |
|
Recoating internal |
Min:3Hrs,Max:26Hrs |